用扫描热膨胀显微镜(SThEM)测量木材细胞壁玻璃相变温度分布( Glass-Transition Temperature Profile Measured in a Wood Cell Wall Using Scanning Thermal Expansion Microscope (SThEM) )

JS Antoniow JE Maigret C Jensen… Experimental/ bio-inspired materials elastic moduli elasticity glass transition polymers surface topography thermal expansion/ elastic modulus probe-tip temperatures surface topography plant cell walls lignocellulosic biopolymers spatial distribution scanning thermal expansion microscopy wood cell wall glass transition temperature temperature 20 degC to 250 degC/ A6470P Glass transitions A6570 Thermal expansion and thermomechanical effects A6820 Solid surface structure A8140J Elasticity and anelasticity A6140K Structure of polymers, elastomers, and plastics A6220D Elasticity, elastic constants/ temperature 2.9315E+02 to 5.2315E+02 K

植物细胞壁的主要木质纤维素生物聚合物。利用扫描热膨胀显微镜对杨树细胞壁的横切面进行了研究。在探针尖端温度范围内绘制表面形貌，以捕捉样品表面热膨胀随温度的变化。在20°C至250°C的不同温度下，对热膨胀的空间变化进行了定量的映射。由于玻璃化转变对热膨胀系数和弹性模量的影响很大，因此提取了每个地形图像的相同数据线，以识别其地形演化中作为温度函数的特定热事件。特别是，在细胞壁上，接触面的热膨胀是不均匀的，因此，玻璃化转变温度的分布可以根据在细胞壁结构组织中起作用的木质纤维素聚合物的迁移率来证明和量化。

SciDown文献求助系统（解决99%问题） Public Download Springer Springer dx.doi.org adsabs.harvard.edu ResearchGate ResearchGate forest.ckcest.cn hal.univ-nantes.fr infona.pl hal.archives-ouvertes.fr hal.in2p3.fr hal.cirad.fr hal.univ-brest.fr jeannicod.ccsd.cnrs.fr 118.145.16.217 onacademic.com